http://rdf.ncbi.nlm.nih.gov/pubchem/patent/KR-102341903-B1
Outgoing Links
Predicate | Object |
---|---|
classificationCPCAdditional | http://rdf.ncbi.nlm.nih.gov/pubchem/patentcpc/C08J2329-04 |
classificationCPCInventive | http://rdf.ncbi.nlm.nih.gov/pubchem/patentcpc/C08L29-04 http://rdf.ncbi.nlm.nih.gov/pubchem/patentcpc/C08J5-18 |
classificationIPCInventive | http://rdf.ncbi.nlm.nih.gov/pubchem/patentipc/C08L29-04 http://rdf.ncbi.nlm.nih.gov/pubchem/patentipc/C08J5-18 |
filingDate | 2014-12-17-04:00^^<http://www.w3.org/2001/XMLSchema#date> |
grantDate | 2021-12-21-04:00^^<http://www.w3.org/2001/XMLSchema#date> |
publicationDate | 2021-12-21-04:00^^<http://www.w3.org/2001/XMLSchema#date> |
publicationNumber | KR-102341903-B1 |
titleOfInvention | Film |
abstract | (Project) To provide a film containing polyvinyl alcohol, which has little coloration by heating and is excellent in the dispersed state even when it contains a surfactant. (Solution) A film containing polyvinyl alcohol having a saponification degree of 50 to 99.99 mol% and a viscosity average degree of polymerization of 200 to 5,000, wherein the content of the alkali metal salt of carboxylic acid is 0.5 mass% or less in terms of the mass of the alkali metal, The peak top molecular weight (A) measured by a differential refractive index detector when the polyvinyl alcohol heated at 120° C. for 3 hours was measured by gel permeation chromatography, and an absorption spectrophotometer (measured with a measurement wavelength of 280 nm) The peak top molecular weight (B) used is the following formula (1) (A-B)/A < 0.75 (1) is satisfied, and the absorbance at the peak top molecular weight (B) is 0.25×10 −3 to 3.00×10 −3 . |