abstract |
The present invention relates to a high strength inorganic polymeric mortar composition comprising 25.0 to 43.0 parts by weight of a calcium hydroxide binder consisting of portland cement, alumina cement and blast furnace slag powder, 36.0 to 45.0 parts by weight of silicon oxide, 0.1 to 3.0 parts by weight of a polypropylene fiber, a glass fiber, a carbon fiber, and a polyvinyl alcohol fiber Tin oxide, tin oxide, antimony tin oxide (ATO), indium tin oxide (ITO), aluminum zinc oxide (AZO), cesium And 1 to 3 parts by weight of a nanocomposite powder composed of any one or more of metal oxide nanoparticles and nano-silica is mixed, And the high strength inorganic polymer mortar composition is used in admixture with water. |