http://rdf.ncbi.nlm.nih.gov/pubchem/patent/KR-101015738-B1
Outgoing Links
Predicate | Object |
---|---|
classificationCPCInventive | http://rdf.ncbi.nlm.nih.gov/pubchem/patentcpc/C08G73-06 http://rdf.ncbi.nlm.nih.gov/pubchem/patentcpc/C08G77-455 http://rdf.ncbi.nlm.nih.gov/pubchem/patentcpc/C08G77-54 |
classificationIPCInventive | http://rdf.ncbi.nlm.nih.gov/pubchem/patentipc/C09D179-08 http://rdf.ncbi.nlm.nih.gov/pubchem/patentipc/C08G59-40 http://rdf.ncbi.nlm.nih.gov/pubchem/patentipc/C08G73-06 http://rdf.ncbi.nlm.nih.gov/pubchem/patentipc/C08G77-54 http://rdf.ncbi.nlm.nih.gov/pubchem/patentipc/C08G77-00 http://rdf.ncbi.nlm.nih.gov/pubchem/patentipc/C08G77-455 http://rdf.ncbi.nlm.nih.gov/pubchem/patentipc/C09D163-00 http://rdf.ncbi.nlm.nih.gov/pubchem/patentipc/C09D183-10 http://rdf.ncbi.nlm.nih.gov/pubchem/patentipc/C09D183-08 |
filingDate | 2004-06-01-04:00^^<http://www.w3.org/2001/XMLSchema#date> |
grantDate | 2011-02-22-04:00^^<http://www.w3.org/2001/XMLSchema#date> |
publicationDate | 2011-02-22-04:00^^<http://www.w3.org/2001/XMLSchema#date> |
publicationNumber | KR-101015738-B1 |
titleOfInvention | Siloxane copolymer, its production method and thermosetting resin composition using the same |
abstract | The present invention relates to a siloxane copolymer having a structure represented by the following formula.n n n n n n n n The silicone copolymer of the present invention has the property of easily forming a cured resin film by heat treatment at a relatively low temperature. This cured resin film also has high resistance to organic solvents such as ketones, and is excellent in adhesion, adhesion and durability to metal substrates such as copper even under high humidity conditions.n n n Silicone copolymer, heat treatment, cured resin film, thermosetting resin composition, siloxane copolymer, adhesiveness, adhesion, durability |