http://rdf.ncbi.nlm.nih.gov/pubchem/patent/KR-100670621-B1
Outgoing Links
Predicate | Object |
---|---|
classificationCPCAdditional | http://rdf.ncbi.nlm.nih.gov/pubchem/patentcpc/C01P2004-54 http://rdf.ncbi.nlm.nih.gov/pubchem/patentcpc/C01P2006-12 http://rdf.ncbi.nlm.nih.gov/pubchem/patentcpc/C01P2004-04 |
classificationCPCInventive | http://rdf.ncbi.nlm.nih.gov/pubchem/patentcpc/H01B1-08 http://rdf.ncbi.nlm.nih.gov/pubchem/patentcpc/C01G15-00 http://rdf.ncbi.nlm.nih.gov/pubchem/patentcpc/C01G19-00 |
classificationIPCInventive | http://rdf.ncbi.nlm.nih.gov/pubchem/patentipc/C01G19-00 http://rdf.ncbi.nlm.nih.gov/pubchem/patentipc/C01G15-00 http://rdf.ncbi.nlm.nih.gov/pubchem/patentipc/H01B1-08 |
filingDate | 2002-06-05-04:00^^<http://www.w3.org/2001/XMLSchema#date> |
grantDate | 2007-01-17-04:00^^<http://www.w3.org/2001/XMLSchema#date> |
publicationDate | 2007-01-17-04:00^^<http://www.w3.org/2001/XMLSchema#date> |
publicationNumber | KR-100670621-B1 |
titleOfInvention | Tin-containing indium oxide, a preparation method thereof, a coating liquid using the indium oxide, and an electrically conductive coating formed from the indium oxide |
abstract | An alkali solution is added to the hydrochloric acid solution containing In and Sn at 20 ° C. to adjust the pH to be 3. The temperature of the mixed solution is raised to 90 ° C. and the pH is adjusted to 7.5 by further adding an alkaline solution. The precipitate thus obtained is recovered by filtration, dehydrated and dried to produce Sn-containing indium hydroxide. The indium hydroxide was introduced into a tubular furnace and calcined at a temperature of 600 ° C. for 2 hours in a nitrogen gas atmosphere containing water vapor and NH 3 gas, thereby having a long axis of 0.041 μm, a short axis of 0.025 μm, and a 1.64 A plate-shaped Sn-containing indium oxide having a long axis / short axis ratio is produced.n n n The weight ratio of the acicular ITO particles and the granular ITO particles is mixed at a ratio in the range of 2:98 to 98: 2 to prepare an ITO powder having a SnO 2 content of 2 to 20% by weight. The coating liquid prepared from this mixed ITO powder is applied to form a transparent conductive film having a sheet resistance of 10 Pa / □ or less, a light transmittance of 80% or more, and a haze value of 2% or less. |
isCitedBy | http://rdf.ncbi.nlm.nih.gov/pubchem/patent/KR-101279541-B1 http://rdf.ncbi.nlm.nih.gov/pubchem/patent/US-8624252-B2 http://rdf.ncbi.nlm.nih.gov/pubchem/patent/KR-101234003-B1 |
priorityDate | 2001-08-13-04:00^^<http://www.w3.org/2001/XMLSchema#date> |
type | http://data.epo.org/linked-data/def/patent/Publication |
Incoming Links
Total number of triples: 38.