| abstract |
The object of the present invention is to deploy an air bag composed of a woven fabric made of polyamide fibers having excellent heat resistance when deployed with an inflator gas, without gas loss, and as a result, an excessive amount of generated gas is not required. The airbag module according to the present invention is a woven fabric made of polyamide fiber, and the air permeability of the woven fabric under a pressure of 200 kPa is 10 to 200 cc / cm. 2 / sec, the initial load is 0.02 cN / dtex, the yarn length is 25 cm, and the thermal stress of the constituent yarn measured at a heating rate of 80 ° C./min. The total thermal stress of warp and weft at 230 ° C. It is comprised from the textile fabric for airbags characterized by the sum being 0.33-1.20 cN / dtex. |