http://rdf.ncbi.nlm.nih.gov/pubchem/patent/JP-H10244361-A
Outgoing Links
| Predicate | Object |
|---|---|
| assignee | http://rdf.ncbi.nlm.nih.gov/pubchem/patentassignee/MD5_a10812aeff7304558967cf7f24dfc7fd |
| classificationIPCInventive | http://rdf.ncbi.nlm.nih.gov/pubchem/patentipc/C04B35-66 http://rdf.ncbi.nlm.nih.gov/pubchem/patentipc/B22D41-32 |
| filingDate | 1997-03-04-04:00^^<http://www.w3.org/2001/XMLSchema#date> |
| inventor | http://rdf.ncbi.nlm.nih.gov/pubchem/patentinventor/MD5_27dfefe40d055b2c25f9bf02e4342084 http://rdf.ncbi.nlm.nih.gov/pubchem/patentinventor/MD5_6d78a74b247edb9372523f9c4b174902 |
| publicationDate | 1998-09-14-04:00^^<http://www.w3.org/2001/XMLSchema#date> |
| publicationNumber | JP-H10244361-A |
| titleOfInvention | Unfired alumina-carbon slide plate |
| abstract | (57) [Summary] (Modifications required) [Problem] As a factor that determines the serviceability of a slide gate plate, surface roughening due to the oxidation of carbon due to the inflow of air from the plate surface weakens the tissue. And damage to the nozzle hole edge. Further, in recent years, Ca-added steels which are often produced are often greatly damaged by a reaction between Ca and the aggregate exposed by oxidation of carbon, which contributes to surface roughness and low durability. SOLUTION: As a binder, hexamethylenetetramine is obtained by mixing and pulverizing a resin composition obtained by performing an addition reaction between an alkenyl group of an alkenyl group-containing epoxidized novolak resin and a SiH group of an organopolysiloxane. Unsintered alumina-carbon obtained by adding a silicone-modified phenol resin in an amount of 0.5 to 10% by weight based on 100 parts by weight of an aggregate and kneading, molding, and drying, and having high oxidation resistance. Provide a quality slide gate plate. |