http://rdf.ncbi.nlm.nih.gov/pubchem/patent/JP-H09267073-A
Outgoing Links
| Predicate | Object |
|---|---|
| assignee | http://rdf.ncbi.nlm.nih.gov/pubchem/patentassignee/MD5_5198a2a21392d6cbc0bb4898b3fb3d29 |
| classificationIPCInventive | http://rdf.ncbi.nlm.nih.gov/pubchem/patentipc/C23C28-00 http://rdf.ncbi.nlm.nih.gov/pubchem/patentipc/B32B15-08 http://rdf.ncbi.nlm.nih.gov/pubchem/patentipc/B05D7-14 http://rdf.ncbi.nlm.nih.gov/pubchem/patentipc/C23C22-24 http://rdf.ncbi.nlm.nih.gov/pubchem/patentipc/B05D7-24 http://rdf.ncbi.nlm.nih.gov/pubchem/patentipc/B05D3-02 |
| filingDate | 1996-04-01-04:00^^<http://www.w3.org/2001/XMLSchema#date> |
| inventor | http://rdf.ncbi.nlm.nih.gov/pubchem/patentinventor/MD5_23e63143aa121447029b9b558c706294 http://rdf.ncbi.nlm.nih.gov/pubchem/patentinventor/MD5_9b3cc02e0a787216d444b0f5629b3b1a http://rdf.ncbi.nlm.nih.gov/pubchem/patentinventor/MD5_8f80d9bef9ad29cc759ab9c4bdd90c08 http://rdf.ncbi.nlm.nih.gov/pubchem/patentinventor/MD5_9e95feaeb49205974e300aad2940e74a http://rdf.ncbi.nlm.nih.gov/pubchem/patentinventor/MD5_f9b17479aefbf87ac0f34f71cdeda243 |
| publicationDate | 1997-10-14-04:00^^<http://www.w3.org/2001/XMLSchema#date> |
| publicationNumber | JP-H09267073-A |
| titleOfInvention | Method for producing surface-treated steel sheet with excellent press workability |
| abstract | (57) Abstract: A lubricant layer on the surface prevents direct contact between a resin and a mold, and particles dispersed in the coating film are constantly coated even when the coating film is severely deformed during deep drawing. Provided is a method for producing a surface-treated steel sheet with excellent press workability, which enables a coating having a structure in which lubrication is replenished from the inside and good lubrication workability is maintained by high-speed passing through high-temperature short-time baking. thing. SOLUTION: An ether ester type urethane resin and an epoxy resin with silica 1 After applying a water-based lubricating paint containing 0-40%, 3-30% polyolefin wax, and 2-10% high-boiling solvent, baking is performed by step heating by induction heating at a furnace atmosphere temperature of 300 ° C or less. Lubrication film thickness 0.3 ~ in 2 to 8 seconds A method for producing a surface-treated steel sheet having excellent press working characteristics, which has a thickness of 5 μm and has a surface lubricant coating layer thickness of 0.04 to 1 μm formed on a lubricating layer. |
| isCitedBy | http://rdf.ncbi.nlm.nih.gov/pubchem/patent/CN-1297688-C http://rdf.ncbi.nlm.nih.gov/pubchem/patent/WO-02057510-A1 http://rdf.ncbi.nlm.nih.gov/pubchem/patent/CN-100354050-C http://rdf.ncbi.nlm.nih.gov/pubchem/patent/US-8709550-B2 http://rdf.ncbi.nlm.nih.gov/pubchem/patent/CN-100368098-C |
| priorityDate | 1996-04-01-04:00^^<http://www.w3.org/2001/XMLSchema#date> |
| type | http://data.epo.org/linked-data/def/patent/Publication |
Incoming Links
Total number of triples: 47.