http://rdf.ncbi.nlm.nih.gov/pubchem/patent/JP-H08277166-A
Outgoing Links
Predicate | Object |
---|---|
assignee | http://rdf.ncbi.nlm.nih.gov/pubchem/patentassignee/MD5_f1192a135e4bc40a5f201a9646f20172 http://rdf.ncbi.nlm.nih.gov/pubchem/patentassignee/MD5_d9cb217f83556ce2a418344c2d485415 |
classificationIPCInventive | http://rdf.ncbi.nlm.nih.gov/pubchem/patentipc/C04B35-593 http://rdf.ncbi.nlm.nih.gov/pubchem/patentipc/C04B35-584 http://rdf.ncbi.nlm.nih.gov/pubchem/patentipc/C04B35-626 |
filingDate | 1995-03-31-04:00^^<http://www.w3.org/2001/XMLSchema#date> |
inventor | http://rdf.ncbi.nlm.nih.gov/pubchem/patentinventor/MD5_e0142f92aeba1df5ea802a44e847a1ff http://rdf.ncbi.nlm.nih.gov/pubchem/patentinventor/MD5_884904fdb49d8f3e09d6dbb16a01548a http://rdf.ncbi.nlm.nih.gov/pubchem/patentinventor/MD5_41cfae340a9ee80a1757d90e3656b979 |
publicationDate | 1996-10-22-04:00^^<http://www.w3.org/2001/XMLSchema#date> |
publicationNumber | JP-H08277166-A |
titleOfInvention | Silicon nitride powder for silicon nitride sintered body, silicon nitride sintered body and method for producing the same |
abstract | (57) [Summary] [Objective] A dense silicon nitride having a high fracture toughness value and excellent strength at a lower sintering temperature than when using β-type silicon nitride powder produced by a conventional direct nitriding method as a raw material. Obtain an elementary sintered body. [Structure] A nitrogen-containing silane compound and / or a sintered powder of an amorphous silicon nitride powder, and a β-type silicon nitride 8 0% by weight or more, a rare earth compound is contained in a concentration of 0.05 to 2.0% by weight based on a metal element, the average particle diameter of the constituent particles is 0.1 μm or more and 0.5 μm or less, and the aspect ratio is 2. Using β-type silicon nitride powder controlled to 5 or less, one or more selected from magnesium oxide, aluminum oxide, and oxides of Group IIIa elements of the periodic table After the addition of 0.2 to 6% by weight of the oxide of 1 to 100, the mixture is molded into 1 to 19 at 1 to 100 atm under nitrogen or a nitrogen-containing inert gas atmosphere. By firing at a temperature of 00 ° C. until the bulk density reaches 95% or more of the theoretical density, a silicon nitride sintered body having a high fracture toughness value and excellent strength is obtained. |
isCitedBy | http://rdf.ncbi.nlm.nih.gov/pubchem/patent/CN-111727168-A |
priorityDate | 1995-03-31-04:00^^<http://www.w3.org/2001/XMLSchema#date> |
type | http://data.epo.org/linked-data/def/patent/Publication |
Incoming Links
Total number of triples: 46.