(57) [Summary] [Object] To provide a method for producing a propylene-based resin molded product having high crystallinity, excellent rigidity and heat resistance, and particularly having a significantly high heat distortion temperature. [Structure] An amide compound is blended in a proportion of 0.0001 to 10 parts by weight with respect to 100 parts by weight of a propylene resin, and this is melted at a temperature equal to or higher than a melting temperature of the amide compound in a melt of the propylene resin. A method for producing a propylene-based resin molded product, which comprises kneading and then cooling to obtain a molding material, and molding the material at a temperature lower than the melting temperature of the amide compound. |