Predicate |
Object |
assignee |
http://rdf.ncbi.nlm.nih.gov/pubchem/patentassignee/MD5_f95e92e0fb1e1198b34494bd59d56f2e |
classificationCPCAdditional |
http://rdf.ncbi.nlm.nih.gov/pubchem/patentcpc/Y02E60-10 |
classificationIPCInventive |
http://rdf.ncbi.nlm.nih.gov/pubchem/patentipc/H01M4-52 http://rdf.ncbi.nlm.nih.gov/pubchem/patentipc/B82Y99-00 http://rdf.ncbi.nlm.nih.gov/pubchem/patentipc/H01M4-38 http://rdf.ncbi.nlm.nih.gov/pubchem/patentipc/H01M4-62 http://rdf.ncbi.nlm.nih.gov/pubchem/patentipc/H01M10-30 http://rdf.ncbi.nlm.nih.gov/pubchem/patentipc/H01M10-24 http://rdf.ncbi.nlm.nih.gov/pubchem/patentipc/H01M4-32 |
filingDate |
1991-09-13-04:00^^<http://www.w3.org/2001/XMLSchema#date> |
inventor |
http://rdf.ncbi.nlm.nih.gov/pubchem/patentinventor/MD5_775c1c31d414ff42163e5f111985b004 http://rdf.ncbi.nlm.nih.gov/pubchem/patentinventor/MD5_360e7b1ca5cc0acd9f319b63632ee321 http://rdf.ncbi.nlm.nih.gov/pubchem/patentinventor/MD5_7957ca3c1be95eaebc6ff5104cf41762 http://rdf.ncbi.nlm.nih.gov/pubchem/patentinventor/MD5_1ed7a9e98725ac0f30805e823d7d8363 |
publicationDate |
1994-10-07-04:00^^<http://www.w3.org/2001/XMLSchema#date> |
publicationNumber |
JP-H06283170-A |
titleOfInvention |
Nickel-hydrogen battery |
abstract |
(57) [Abstract] [Purpose] To provide a nickel-hydrogen battery having excellent charging efficiency at high temperature and having a small self-discharge amount. [Structure] Nickel hydroxide powder in which 7 wt% zinc and 3 wt% cobalt are solid-dissolved while suppressing the development of internal transition pores having a pore radius of 30 Å or more and controlling the pore volume to 0.1 ml / g or less. A 10% by weight CoO powder was mixed with an aqueous solution in which 1% of carboxymethyl cellulose was dissolved to prepare a fluid paste solution, which was filled in a predetermined amount on a nickel fiber substrate having a porosity of 95%, dried and pressed to form a nickel electrode. did. On the other hand, 3% PVA aqueous solution was added to hydrogen-absorbing alloy powder to form a paste, which was filled into a nickel fiber substrate similar to the positive electrode, dried and pressed to obtain MmNi 3.7 Al 0.3 Co. To obtain a hydrogen storage electrode of 0.7 Fe 0 .3. A nickel-hydrogen battery was obtained by combining these. |
isCitedBy |
http://rdf.ncbi.nlm.nih.gov/pubchem/patent/WO-2005014871-A1 http://rdf.ncbi.nlm.nih.gov/pubchem/patent/US-8535460-B2 http://rdf.ncbi.nlm.nih.gov/pubchem/patent/DE-3934792-A1 http://rdf.ncbi.nlm.nih.gov/pubchem/patent/JP-2020198187-A http://rdf.ncbi.nlm.nih.gov/pubchem/patent/CN-112018456-A http://rdf.ncbi.nlm.nih.gov/pubchem/patent/US-9219277-B2 |
priorityDate |
1991-09-13-04:00^^<http://www.w3.org/2001/XMLSchema#date> |
type |
http://data.epo.org/linked-data/def/patent/Publication |