| abstract |
(57) [Summary] (Corrected) [Purpose] Primer coating or plasma irradiation treatment is applied without the need for pretreatment with halogenated organic solvent. After that, the top coat can be applied, the adhesion of the coating film and the gaso resistance Provided is an impact-resistant polypropylene resin composition capable of obtaining a molded product having good curability. [Constitution] (A) Polypropylene, (B) Propylene content is 15 to 50% by weight, Mooney viscosity ML 1 + 4 (10 Ethylene oxide-propylene-diene terpolymer rubber having an iodine value of 8 to 25, an Mw / Mn of 1.5 to 4.0, and a (C) propylene content of 15 to 35. % By weight, Mooney viscosity ML 1 + 4 (100 ° C) is 15 to 2 The ethylene-propylene copolymer rubber of No. 5, polyhydroxy polyolefin (D) having a hydroxyl value (KOHmg / g) of 20 or more, and (E) an inorganic filler. |