| abstract |
(57) [Summary] [Purpose] To provide a method for producing a stainless steel plate having low whiteness and having both antiglare property and corrosion resistance. [Constitution] Weight%, C: 0.020% or less, Cr: 1 7.0-35.0%, Mo: 0.5-4.0%, Cr + 3Mo: 26-40%, Si: 0.05-1.0%, M n: 0.05 to 0.5%, Al: 0.005 to 0.2 %, The balance Fe and other unavoidable impurities, and a bright-annealed cold-rolled steel sheet having a surface roughness (Ra) of the steel sheet of 0.5 to 10.0 μm, and an acid solution of sulfuric acid or hydrochloric acid alone or in combination of one or more. It is pickled with, and immersed in a solution containing nitric acid. Further, the stainless steel plate was Nb: 0.1 to 0. 5%, Ti: 0.1 to 0.5%, V: 0.05 to 0.5 %, Preferably containing at least one element. |