| abstract |
An object of the present invention is to provide a method for producing a molded article having excellent mechanical properties, a cellulose fiber-containing resin composition as a material for the molded article, and a method for producing the same. [1] Polyethylene having a melt flow rate (MFR) of 0.5 to 25 g / 10 min measured under conditions of 190 ° C. and a load of 10 kgf in accordance with JIS K7210, and dispersed in the polyethylene A cellulose fiber-containing resin composition comprising cellulose fiber. [2] The cellulose fiber-containing resin composition according to [1], wherein the cellulose fiber has an average fiber width of 2 to 15,000 nm and an average fiber length of 0.1 to 2.0 mm. [3] The cellulose fiber-containing resin composition according to any one of [1] or [2], wherein at least a part of the cellulose fiber is a cellulose fiber in which at least a part of the hydroxyl group is chemically modified. [Selection figure] None |