| abstract |
The present invention provides an ethylene polymer composition for extrusion laminating that exhibits excellent processability and extrusion characteristics during extrusion molding, and has good heat-resistant glossiness of the extruded product. The ethylene-α-olefin copolymer (A) has a long chain branching and has a density of 920 to 955 kg / m 3 and an MFR of 5 to 20 g / 10 minutes, and a density of 915 to 930 kg / m 3 , MFR 1 to 5 g / 10 min, high pressure method low density polyethylene (B) having a melt tension measured at 190 ° C. of 100 mN or more, 10 to 30 wt% and density 915 to 930 kg / m 3 , MFR 10 to 50 g / 10 min, It is a polyethylene resin composition for extrusion lamination that contains 10 to 30% by weight of a high-pressure method low-density polyethylene (C) having a melt tension measured at 160 ° C. of 100 mN or less and satisfies specific requirements. [Selection figure] None |