http://rdf.ncbi.nlm.nih.gov/pubchem/patent/JP-2011140688-A
Outgoing Links
Predicate | Object |
---|---|
assignee | http://rdf.ncbi.nlm.nih.gov/pubchem/patentassignee/MD5_b27deaf45890893586c2ed77ac13dc32 |
classificationIPCInventive | http://rdf.ncbi.nlm.nih.gov/pubchem/patentipc/C22C38-38 http://rdf.ncbi.nlm.nih.gov/pubchem/patentipc/C21D9-46 http://rdf.ncbi.nlm.nih.gov/pubchem/patentipc/C22C38-06 http://rdf.ncbi.nlm.nih.gov/pubchem/patentipc/C22C38-00 |
filingDate | 2010-01-06-04:00^^<http://www.w3.org/2001/XMLSchema#date> |
inventor | http://rdf.ncbi.nlm.nih.gov/pubchem/patentinventor/MD5_99ac467d51c2dd3fd221c6ed1f61d09f http://rdf.ncbi.nlm.nih.gov/pubchem/patentinventor/MD5_52a0361a158abcfd2fa2e0a1978788a8 http://rdf.ncbi.nlm.nih.gov/pubchem/patentinventor/MD5_77b166c51a2bd8d17403cb30f1de5ccf http://rdf.ncbi.nlm.nih.gov/pubchem/patentinventor/MD5_36beecf541927d4f8537ac40c6f6e0fe http://rdf.ncbi.nlm.nih.gov/pubchem/patentinventor/MD5_78f523c38fa8970f5bfe32bf6a21c314 |
publicationDate | 2011-07-21-04:00^^<http://www.w3.org/2001/XMLSchema#date> |
publicationNumber | JP-2011140688-A |
titleOfInvention | Cold rolled steel sheet manufacturing method |
abstract | A method for producing a high-tensile cold-rolled steel sheet having excellent ductility and stretch flangeability is provided. A method for producing a cold-rolled steel sheet comprising a metallographic structure in which a main phase is ferrite and a second phase includes a low-temperature transformation generation phase, which includes the following steps (A) to (C): (A) By mass%, C: more than 0.010% and less than 0.10%, Si: more than 0.10% and 2.0% or less, Mn: 1.50 to 3.50%, P: 0.10% or less, S: 0.010% or less, sol.Al: 0.10% And a slab having a chemical composition containing N: 0.010% or less is subjected to hot rolling to complete rolling in a temperature range of 3 or more points to form a hot-rolled steel sheet, and the hot-rolled steel sheet is completed for the rolling. After 0.4 seconds, the steel sheet is cooled to a temperature range of 720 ° C or lower and wound in a temperature range of 400 ° C or higher; (B) a cold rolling step of cold rolling the cold rolled steel sheet to the hot rolled steel sheet; and (C) An annealing process in which the cold-rolled steel sheet is subjected to soaking in a temperature range of (Ac 3 point-40 ° C) or higher. [Selection figure] None |
isCitedBy | http://rdf.ncbi.nlm.nih.gov/pubchem/patent/CN-112662933-A http://rdf.ncbi.nlm.nih.gov/pubchem/patent/CN-109161799-A http://rdf.ncbi.nlm.nih.gov/pubchem/patent/EP-2837707-A4 http://rdf.ncbi.nlm.nih.gov/pubchem/patent/WO-2013154071-A1 http://rdf.ncbi.nlm.nih.gov/pubchem/patent/JP-2012017500-A http://rdf.ncbi.nlm.nih.gov/pubchem/patent/US-9809874-B2 http://rdf.ncbi.nlm.nih.gov/pubchem/patent/CN-103882320-A |
priorityDate | 2010-01-06-04:00^^<http://www.w3.org/2001/XMLSchema#date> |
type | http://data.epo.org/linked-data/def/patent/Publication |
Incoming Links
Total number of triples: 27.