| abstract |
[PROBLEMS] To provide a thermoplastic resin composition capable of forming a film insert molded article having excellent rigidity, impact resistance, adhesion, and appearance design, and a film insert molded article comprising the thermoplastic resin composition. To do. An impact is applied to 100 parts by weight of a resin component comprising (A) 100 to 50% by weight of a polycarbonate resin (component A) and (B) 0 to 50% by weight of a resin other than the polycarbonate resin (component B). It contains 0.1 to 30 parts by weight of the modifying material (C component) and (D) 0 to 30 parts by weight of the inorganic filler (D component), and the flexural modulus according to ISO-178 is 2,200 MPa or more, 12, The resin composition for film insert molding characterized by being less than 000 MPa. [Selection figure] None |