Predicate |
Object |
assignee |
http://rdf.ncbi.nlm.nih.gov/pubchem/patentassignee/MD5_e3b0a3dbf8d6c9712d86ea1383fd5327 |
classificationCPCAdditional |
http://rdf.ncbi.nlm.nih.gov/pubchem/patentcpc/C04B2103-32 http://rdf.ncbi.nlm.nih.gov/pubchem/patentcpc/C04B2111-00086 http://rdf.ncbi.nlm.nih.gov/pubchem/patentcpc/C04B2111-72 |
classificationCPCInventive |
http://rdf.ncbi.nlm.nih.gov/pubchem/patentcpc/C04B28-02 |
classificationIPCAdditional |
http://rdf.ncbi.nlm.nih.gov/pubchem/patentipc/C04B111-72 |
classificationIPCInventive |
http://rdf.ncbi.nlm.nih.gov/pubchem/patentipc/C04B24-06 http://rdf.ncbi.nlm.nih.gov/pubchem/patentipc/C04B22-14 http://rdf.ncbi.nlm.nih.gov/pubchem/patentipc/C04B22-10 http://rdf.ncbi.nlm.nih.gov/pubchem/patentipc/C04B22-08 http://rdf.ncbi.nlm.nih.gov/pubchem/patentipc/C04B41-61 http://rdf.ncbi.nlm.nih.gov/pubchem/patentipc/C04B28-02 http://rdf.ncbi.nlm.nih.gov/pubchem/patentipc/C04B16-06 http://rdf.ncbi.nlm.nih.gov/pubchem/patentipc/C04B24-24 |
filingDate |
2007-04-26-04:00^^<http://www.w3.org/2001/XMLSchema#date> |
inventor |
http://rdf.ncbi.nlm.nih.gov/pubchem/patentinventor/MD5_9d145bf806dbde6f05d43cda50f5dc8d http://rdf.ncbi.nlm.nih.gov/pubchem/patentinventor/MD5_1373d3a4cac006bb0daa35b8eb0d260e http://rdf.ncbi.nlm.nih.gov/pubchem/patentinventor/MD5_f6422482facdbb362d896c7fa2592b32 http://rdf.ncbi.nlm.nih.gov/pubchem/patentinventor/MD5_3f709c4f5f13f499e6677415dbe75148 |
publicationDate |
2008-11-13-04:00^^<http://www.w3.org/2001/XMLSchema#date> |
publicationNumber |
JP-2008273762-A |
titleOfInvention |
Concrete section repair material |
abstract |
[PROBLEMS] To ensure a long pot life of about 30 to 90 minutes without reducing the compressive strength at a young age (about 3 hours). A concrete cross-section repair material comprises 100 to 300% by mass of an aggregate with respect to 100% by mass of a cement composition containing 100 to 1000% by mass of a cement mineral with respect to 100% by mass of an admixture, and 1 to 20% by mass re-emulsified powder resin and 0.1-2.0% by mass fiber. The admixture contains a setting modifier composed of sodium aluminate, inorganic carbonate and carboxylic acids at a predetermined ratio with respect to the rapid hardening component in which calcium aluminate and inorganic sulfate are mixed at a predetermined mass ratio. The vitrification rate of calcium aluminate is 80% or more, and when any one of the setting modifiers is 100% by mass, the other two types are included in an amount of 60 to 160% by mass. [Selection] Figure 1 |
isCitedBy |
http://rdf.ncbi.nlm.nih.gov/pubchem/patent/JP-2016050163-A http://rdf.ncbi.nlm.nih.gov/pubchem/patent/JP-2013139348-A http://rdf.ncbi.nlm.nih.gov/pubchem/patent/JP-2012533513-A http://rdf.ncbi.nlm.nih.gov/pubchem/patent/JP-2013133271-A http://rdf.ncbi.nlm.nih.gov/pubchem/patent/JP-2018100503-A http://rdf.ncbi.nlm.nih.gov/pubchem/patent/JP-2011016681-A http://rdf.ncbi.nlm.nih.gov/pubchem/patent/JP-2014091669-A http://rdf.ncbi.nlm.nih.gov/pubchem/patent/US-11117833-B2 http://rdf.ncbi.nlm.nih.gov/pubchem/patent/US-10800701-B2 http://rdf.ncbi.nlm.nih.gov/pubchem/patent/KR-20180131532-A |
priorityDate |
2007-04-26-04:00^^<http://www.w3.org/2001/XMLSchema#date> |
type |
http://data.epo.org/linked-data/def/patent/Publication |