| abstract |
PROBLEM TO BE SOLVED: To provide an antiglare hard coat film excellent in hardness, scratch resistance and antiglare property. The antiglare hard coat film 4 of the present invention is an antiglare hard coat film 4 having a hard coat layer 2 containing fine particles 3 on at least one surface of a transparent plastic film substrate 1. The thickness of the hard coat layer 2 is in the range of 15 to 30 μm, the weight average particle size of the fine particles 3 is in the range of 30 to 75% of the thickness of the hard coat layer 2, and the surface of the hard coat layer 2 is The average inclination angle θa of the concavo-convex shape is in the range of 0.4 to 1.5 degrees, and the hard coat layer is formed by using a hard coat forming resin containing three specific types of resin components. And [Selection] Figure 1 |