http://rdf.ncbi.nlm.nih.gov/pubchem/patent/JP-2008081571-A
Outgoing Links
Predicate | Object |
---|---|
assignee | http://rdf.ncbi.nlm.nih.gov/pubchem/patentassignee/MD5_3fedd1aa5fe3bde139f0fbf7bd16550b |
classificationIPCInventive | http://rdf.ncbi.nlm.nih.gov/pubchem/patentipc/C08J7-04 http://rdf.ncbi.nlm.nih.gov/pubchem/patentipc/C08F220-26 |
filingDate | 2006-09-27-04:00^^<http://www.w3.org/2001/XMLSchema#date> |
inventor | http://rdf.ncbi.nlm.nih.gov/pubchem/patentinventor/MD5_ddfdc364ab9423d98f45010709a206b0 http://rdf.ncbi.nlm.nih.gov/pubchem/patentinventor/MD5_576dd291e81a8ec3b70eb9b6d90b7042 |
publicationDate | 2008-04-10-04:00^^<http://www.w3.org/2001/XMLSchema#date> |
publicationNumber | JP-2008081571-A |
titleOfInvention | Hard coat agent and hard coat film |
abstract | PROBLEM TO BE SOLVED: To obtain a hard coat film excellent in surface hardness by reducing warpage due to shrinkage during UV curing. SOLUTION To 100 parts by weight of dipentaerythritol hexaacrylate (solid content: 100%), 32 weight of 2-acryloyloxyethyl-2-hydroxyethylphthalic acid monomer (solid content: 100%, functional group: hydroxyl group). Parts, 208 parts by weight of MEK as a solvent, 7 parts by weight of 1-hydroxycyclohexyl phenyl ketone as an initiator and 0.4 parts by weight of a leveling agent to obtain a hard coat agent A, and then hard coat The agent A is applied to a 100 μm polyethylene terephthalate film by a bar coating method so as to have a cured film thickness of 5 μm, and dried by a hot air dryer at 80 ° C. for 2 minutes. Thereafter, ultraviolet light is irradiated with an integrated light amount of about 300 mJ / cm 2 . [Selection figure] None |
isCitedBy | http://rdf.ncbi.nlm.nih.gov/pubchem/patent/JP-2010215775-A http://rdf.ncbi.nlm.nih.gov/pubchem/patent/JP-2010264750-A http://rdf.ncbi.nlm.nih.gov/pubchem/patent/JP-2010264749-A http://rdf.ncbi.nlm.nih.gov/pubchem/patent/WO-2010119751-A1 http://rdf.ncbi.nlm.nih.gov/pubchem/patent/JP-2011213122-A |
priorityDate | 2006-09-27-04:00^^<http://www.w3.org/2001/XMLSchema#date> |
type | http://data.epo.org/linked-data/def/patent/Publication |
Incoming Links
Total number of triples: 87.