| abstract |
Disclosed is a dielectric ceramic composition capable of achieving both a dielectric constant and a capacity-temperature characteristic even when a dielectric layer is thinned, and a method for producing the same. A main component including a compound having a perovskite structure represented by the formula ABO 3 (A is Ba or Ba and Ca, B is Ti or Ti and Zr), and an oxide of R (R is Y, La, And a fourth subcomponent containing at least one selected from Ce, Pr, Nd, Pm, Sm, Eu, Gd, Tb, Dy, Ho, Er, Tm, Yb, and Lu). A method of manufacturing, wherein the main component material is divided into first and second main component materials, the first main component material and a part of the fourth subcomponent material are reacted in advance to obtain a reacted material; Adding the second main component and the remaining fourth subcomponent material to the reacted raw material, and the number of moles of the first and second main components is n1, n2 mol, 0.5 ≦ n1 / (n1 + n2) ≦ 1. [Selection figure] None |