abstract |
The present invention relates to a moldability in which fine particles are monodispersed without agglomerating into a liquid crystalline resin, have a high storage elastic modulus even in a non-oriented state, and have a reduced crystallization rate despite the inclusion of fine particles. The acquisition of high-rigidity materials with excellent resistance is an issue. Fine particles providing a liquid crystalline resin composition comprising 1 to 5 parts by weight of fine particles having an average particle size of 0.08 μm or more and less than 0.2 μm in 100 parts by weight of a liquid crystalline polyester Amorphous silica or the like is preferable, and when a resin composition is produced, it is preferable to knead at a resin pressure of 1 MPa or more. [Selection figure] None |