| abstract |
The present invention consists of one or more hot melt adhesives in which the hot melt adhesive / filler compound is not dissolved in the hot melt adhesive and one or more fillers in an amount of 50-15% by weight, The hot melt adhesive / filler compound has the following parameters: MVR value 2~6cm 3/10 min, preferably 3 to 5 cm 3/10 min, 2. 2. surface tack / tack measured at 65 ° C. according to DIN EN 14610 at least 10 N / 2 cm, preferably 15 N / 2 cm, in particular 20 N / 2 cm; 3. Adhesion value / peel strength to the surface material and lining measured according to DIN 53357 at least 30 N / 5 cm; A novel for the manufacture of shoes or shoe components in the form of a hot melt adhesive / filler compound, characterized by simultaneously filling up to 25%, preferably less than 20% of the length measured at a temperature of 90 ° C. The present invention relates to a thermoplastic reinforcing material and a method for producing the thermoplastic reinforcing material without polluting the environment. |