http://rdf.ncbi.nlm.nih.gov/pubchem/patent/JP-2004156124-A
Outgoing Links
Predicate | Object |
---|---|
assignee | http://rdf.ncbi.nlm.nih.gov/pubchem/patentassignee/MD5_b576861ef2bbff1956483170b6360884 |
classificationIPCInventive | http://rdf.ncbi.nlm.nih.gov/pubchem/patentipc/C21D8-02 http://rdf.ncbi.nlm.nih.gov/pubchem/patentipc/C22C38-58 http://rdf.ncbi.nlm.nih.gov/pubchem/patentipc/C22C38-04 http://rdf.ncbi.nlm.nih.gov/pubchem/patentipc/C22C38-00 http://rdf.ncbi.nlm.nih.gov/pubchem/patentipc/B23K31-00 |
filingDate | 2002-11-08-04:00^^<http://www.w3.org/2001/XMLSchema#date> |
inventor | http://rdf.ncbi.nlm.nih.gov/pubchem/patentinventor/MD5_5a68453f46e57f6efb3681c70f83c691 http://rdf.ncbi.nlm.nih.gov/pubchem/patentinventor/MD5_98b836282627c7d453902438da035491 http://rdf.ncbi.nlm.nih.gov/pubchem/patentinventor/MD5_4a9baf49407e150691012ca480263300 |
publicationDate | 2004-06-03-04:00^^<http://www.w3.org/2001/XMLSchema#date> |
publicationNumber | JP-2004156124-A |
titleOfInvention | High-pass temperature multi-pass welded steel material, method for producing the same, and high-pass temperature multi-pass weld method. |
abstract | [PROBLEMS] To provide a steel material for high interpass temperature welding having sufficient HAZ toughness even when the interpass temperature reaches 350 ° C. or higher, a method of manufacturing the same, and a welding method using the same. SOLUTION: A step of adding ferromanganese or silicomanganese to molten steel discharged from a converter to preliminarily deoxidize so that the dissolved oxygen amount becomes 0.0030 to 0.0120% (mass ratio, the same applies hereinafter). Adding REM to adjust the dissolved oxygen amount to be 0.0010 to 0.0050% and the remaining amount of REM in the steel to be 0.0010 to 0.03%, and C: 0.03 to 0.03%. 0.15%, Si: 0.05 to 0.50%, Mn: 0.5 to 2.0%, P: 0.03% or less, S: 0.0005 to 0.0080%, REM: 0. The molten steel obtained by sequentially performing the steps of adjusting to a final steel composition containing 0010 to 0.03%, the balance Fe and unavoidable impurities is cast to obtain a steel ingot, and after heating the steel ingot, it is heated to a final product shape. After rolling, to a temperature of 500 ° C or less at a speed of 1 ° C / s or more The recuperation temperature after cooling is stopped while retirement is prepared by a 100 ° C. or less. |
isCitedBy | http://rdf.ncbi.nlm.nih.gov/pubchem/patent/CN-101270443-B |
priorityDate | 2002-11-08-04:00^^<http://www.w3.org/2001/XMLSchema#date> |
type | http://data.epo.org/linked-data/def/patent/Publication |
Incoming Links
Total number of triples: 23.