| abstract |
PROBLEM TO BE SOLVED: To provide a flame-retardant polyolefin-based resin-coated sheet which does not contain a halogen-containing resin and a flame retardant, has excellent mechanical strength, flame resistance, workability, and coloring properties, and is useful as an industrial material. SOLUTION: On both sides of a base fabric including a fabric woven from thermoplastic resin filament yarns, 100 parts by weight of a polyolefin-based resin and 5 to 35 parts by weight of red phosphorus particles are contained. Forming a double-sided resin layer from a polyolefin-based resin composition having a melt flow rate (MFR) of up to 5.0 g / 10 min (according to the test method of JIS K 6760; temperature: 190 ° C., load: 21.18 N) Then, when the obtained resin-coated sheet is heated at 150 ° C. for 15 minutes, the dry heat shrinkage in the warp and weft directions is 5 to 25%. |