| abstract |
(57) [Abstract] (Modified) [Problem] A foam molded article excellent in recyclability and disposal property, capable of simplifying a production process, and having a good balance of flexibility, heat resistance and impact resistance. The present invention provides a thermoplastic resin composition for foaming capable of obtaining the following. SOLUTION: It contains the following components (A) and (B), A thermoplastic resin composition for foaming, wherein the weight ratio of (A) / (B) is from 95/5 to 5/95. (A): Amorphousness in which the flexural modulus (Ua (MPa)) of the resin composition (b) obtained by blending with the homopolypropylene resin (a) measured according to JIS K7203 satisfies the following formula (1). Olefin (co) polymer Ua ≦ 1.5 × Sa × (Ta / 100) 3.3 (1) (Sa represents the flexural modulus (MPa) measured according to JIS K7203 of (a), and Ta represents the content (% by weight) of (a) in (b).) (B) ): Thermoplastic resin (however, excluding the above (A)) |