abstract |
Disclosed is a calcined alumina which has a BET specific surface area of 10 to 20 m2 / g, a main crystalline phase consisting of an α phase, substantially without θ phase, and an average particle size of 0.5 m or less, a process for producing this calcined alumina and a fine powder of α-alumina obtained by means of this calcined alumina. |