| abstract |
A process for the manufacture of a decorative surface element, said element comprising a base layer, a decoration and a wear layer of a UV or electron-cured enamel, the wear layer comprising hard particles with an average size of particles in the range of 50 nanometers - 150 micrometers, in which one or more structured surfaces forming stamping surfaces of one or more rollers or molds that are heated to a surface temperature above 40 ° C, preferably in the range of 50 ° C - 150 ° C, are located above the decorative enameled surface after the enamel has been cured until it reaches a desired viscosity, and they are pressed continuously or discontinuously with a pressure of 50-200 bar, preferably 65-100 bar, whereby The enamel will be provided with a surface structure that improves the decorative effect of the decoration, for which one or more rodil The glazing is pressed into the structured wear surface layer with glazing rollers that are heated to a surface temperature above 30 ° C, preferably in the range of 35 ° C - 100 ° C, whereby the wear layer is completely cured. |