| abstract |
To provide a propylene polymer composition that is capable of giving shaped article with excellent rigidity. A propylene polymer composition includes a propylene homopolymer (A) having an intrinsic viscosity [η] measured in a tetralin solvent at 135°C in the range of 7 to 12 dl/g, a propylene polymer (B) having an intrinsic viscosity [η] measured in a tetralin solvent at 135°C in the range of not less than 0.21 dl/g and less than 0.54 dl/g, and having a proportion of a component eluted at a temperature of not more than -20°C in TREF in the range of not more than 3.5 mass%, and a propylene polymer (C) having an intrinsic viscosity [η] measured in a tetralin solvent at 135°C in the range of not less than 0.54 dl/g and less than 2.6 dl/g, wherein the content of (A) is 0.5 to 47.5 mass%, the content of (B) is 5 to 95 mass% and the content of (C) is 2.5 to 85.5 mass%, based on the total of (A), (B) and (C). |