A rubber composition with disperse phase particles containing poly(phenylene ether) can be formed by a method that includes melt blending an uncured rubber with a poly(phenylene ether) composition containing a poly(phenylene ether) and an oil to form an uncured rubber composition, then curing the uncured rubber composition. Before being blended with the rubber, the poly(phenylene ether) composition exhibits a glass transition temperature of about 40 to about 140o C, and during blending with the rubber, the oil component of poly(phenylene ether) composition migrates from the poly(phenylene ether) composition to the rubber, leaving a poly(phenylene ether)-containing disperse phase that gives rise to a second hysteresis peak temperature of about 160 to about 220oC as measured by dynamic mechanical analysis of the cured rubber composition. Also described are the poly(phenylene ether) composition used in the method, a cured rubber composition formed by the method, and a tire containing the cured rubber composition. |