| abstract |
Provided is a method for manufacturing an oxide superconductor, including preparing a coating solution containing alcohols including methanol as a solvent, the coating solution dissolving fluorocarboxylic acid salts including trifluoroacetates, the trifluoroacetates including a metal, barium and copper, the metal being selected from yttrium and lanthanoid metals (provided that cerium, praseodymium, promethium, and ruthenium are excluded); adding a substance of formula: CF 2 H-(CF 2 ) n -COOH or HOCO-(CF 2 ) m -COOH (wherein n and m represent positive integers) as a crack preventing chemical to the coating solution; forming a gel film on a substrate using the coating solution having the crack preventing chemical added thereto; forming a calcined film by calcining the gel film at an oxygen partial pressure of 3% or less in a process that is maintained at 200°C or higher for a total time of 7 hours or less; and forming an oxide superconductor film by firing and oxygen anneal of the calcined film. |