| abstract |
Disclosed are a piping member formed by using a propylene-based resin composition comprising 100 parts by mass of a propylene-ethylene random copolymer (A) having an ethylene content of 2 to 5%, a crystallization temperature of 86 to 105°C, a melt flow rate of 0.01 to 2.00 g/10 min and a molecular weight distribution of 3 to 8, and 1 to 15 parts by mass of a styrene-butadiene-base rubber (B) having a styrene content of 10 to 40% and a weight average molecular weight of 200,000 or more as essential components, a melt flow rate after kneading being from 0.01 to 2.00 g/10 min, characterized in that the propylene-based resin composition further comprising a hindered amine-based light stabilizer (C) having a weight average molecular weight of 2,000 or more in the amount of 0.1 to 1.0 parts by mass based on 100 parts by mass of the propylene-ethylene random copolymer; and a piping member formed by using a propylene-based resin composition, wherein the styrene-butadiene-base rubber is a hydrogenated styrene-butadiene block copolymer rubber. |