| abstract |
A rubber laminate comprised of a cross-linked rubber layer containing a carboxyl-group containing nitrile copolymer rubber (A), a carboxyl-group containing acryl-based polymer (B), and a specific phosphonium salt and a fluorine-based polymer layer. Preferably, the carboxyl-group content per 100 grams of the (A) ingredient is 2×10 -3 to 1×10 -1 equivalents and the carboxyl-group content per 100 grams of the (B) ingredient is 4×10 -4 to 1×10 -1 equivalents, the (A) ingredient and (B) ingredient are in a weight ratio of 40:60 to 90:10, and the phosphonium salt content in the cross-linked rubber layer is 0.5 to 10 parts by weight per 100 parts by weight of the total of the (A) ingredient and (B) ingredient. According to the present invention, there is provided a rubber laminate excellent in oil resistance and gasoline permeation resistance plus tensile strength, low compression set, and other mechanical characteristics, ozone resistance, and interlayer adhesion. |