| abstract |
To provide a sialon-based phosphor capable of forming a thin film by mixing it with a resin, and giving a uniform photoluminescent light with high light emission intensity, and to provide a method for producing a sialon-based phosphor not having excessively large agglomerated particles and a wide particle size distribution, there is provided a method for producing an ±-sialon based phosphor represented by the formula: n M x Ln y Si 12-(m+n) Al (m+n) O n N 16-n nwherein M is at least one metal selected from Ca, Mg, Y and Li, Ln is at least one lanthanide metal selected from Eu, Dy, Er, Tb, Yb and Ce, ax+by=m (assuming that the valence of metal M is a and the valence of lanthanide metal Ln is b), 0<x¤1.5, 0.3¤m<4.5, and 0<n<2.25), wherein the silicon nitride raw material used as the raw material is a silicon nitride raw material powder comprising amorphous silicon nitride and crystalline silicon nitride. |