| abstract |
The present invention concerns nucleated propylene polymers having a xylene soluble fraction at 23° C. of less than 2.5%, a crystallization temperature of over 124 ° C. and a tensile modulus of greater than 2,000 MPa. These polymers can be prepared by nucleating a propylene polymer with a polymeric nucleating agent containing vinyl compound units, and by polymerizing propylene optionally with comonomers in the presence of a Ziegler-Natta catalyst system primarily transesterified with a phthalic acid ester-a lower alcohol pair to provide said propylene polymer. The catalyst contains a strongly coordinating external donor. |