| abstract |
A transparent brittle, film prepared from a resin composition comprising (A) 100 parts by weight of a vinyl chloride resin, (B) 20 to 200 parts by weight of an acrylic resin, (C) 20 to 250 parts by weight of fused silica comprising aggregates of particles having an average particle diameter in the range of 5 to 20 µm and individual particle diameters in the range of 0.5 to 100 µm or aluminum hydroxide or barium sulfate comprising aggregates of particles having an average particle diameter in the range of 1 to 20 µm and individual particle diameters in the range of 0.2 to 50 µm, (D) 0 to 40 parts by weight of a plasticizer, and (E) 0.5 to 10 parts by weight of a stabilizer. The film is brittle, easily torn, and transparent, has a suitable degree of flexibility and hardness, and can be produced inexpensively and easily. |