| abstract |
A thermoplastic resin composition based on a polyphenylene ether resin and a polyamide resin and having remarkably improved moldability and impact strength at a lower temperature contains 30 to 70 parts by weight of a polyphenylene ether resin (a), 70 to 30 parts by weight of a polyamide resin (b), per 100 parts by weight of the total amount of (a) and (b), 2 to 40 parts by weight of a hydrogenated A-B-A structured block copolymer elastomer (c) per 100 parts by weight of (a), 2 to 60 parts by weight of a polypropylene resin (d) per 100 parts by weight of (a), 0.01 to 10 parts by weight of a compatibilizer (e) per 100 parts by weight of (a), and 2 to 40 parts by weight of an ethylene-α-olefin copolymer modified with an unsaturated acid or acid anhydride per 100 parts by weight of (b). |