abstract |
A propylene-ethylene block copolymer from which molded products having high rigidity and superior high-impact properties can be prepared even without adding any particular additive, is provided, which copolymer is obtained by (i) polymerizing propylene in 70 to 95 weight % based on the total polymerized amount, using a catalyst obtained by reacting an organoaluminum compound (1) or a reaction product of (1) with an electron donor (A), with TiCâ„“ 4 , further reacting the resulting solid product (II) with (A) and an electron acceptor (B), and combining the resulting solid product (III) with an organoaluminum compound (IV) and an aromatic carboxylic acid ester (V), the molar ratio of (V) to (III) being 0.1 to 10.0, and then (ii) polymerizing ethylene or ethylene and propylene in 30 to 5 weight % based on the total polymerized amount, at one or more stages, using the same catalyst as above, the ethylene content being 3 to 20 weight % based on the total polymerized amount. |