http://rdf.ncbi.nlm.nih.gov/pubchem/patent/CN-114717484-A
Outgoing Links
Predicate | Object |
---|---|
assignee | http://rdf.ncbi.nlm.nih.gov/pubchem/patentassignee/MD5_53b4d53983adbf56dd0e7d0bf96f8ce5 |
classificationCPCAdditional | http://rdf.ncbi.nlm.nih.gov/pubchem/patentcpc/Y02P10-20 |
classificationCPCInventive | http://rdf.ncbi.nlm.nih.gov/pubchem/patentcpc/C21D6-008 http://rdf.ncbi.nlm.nih.gov/pubchem/patentcpc/C22C33-04 http://rdf.ncbi.nlm.nih.gov/pubchem/patentcpc/C21D6-002 http://rdf.ncbi.nlm.nih.gov/pubchem/patentcpc/C21D6-005 http://rdf.ncbi.nlm.nih.gov/pubchem/patentcpc/C22C38-38 http://rdf.ncbi.nlm.nih.gov/pubchem/patentcpc/C22C38-34 http://rdf.ncbi.nlm.nih.gov/pubchem/patentcpc/C22C38-22 |
classificationIPCInventive | http://rdf.ncbi.nlm.nih.gov/pubchem/patentipc/C21D6-00 http://rdf.ncbi.nlm.nih.gov/pubchem/patentipc/C22C38-22 http://rdf.ncbi.nlm.nih.gov/pubchem/patentipc/C22C38-38 http://rdf.ncbi.nlm.nih.gov/pubchem/patentipc/C22C38-34 http://rdf.ncbi.nlm.nih.gov/pubchem/patentipc/C22C33-04 |
filingDate | 2021-01-06-04:00^^<http://www.w3.org/2001/XMLSchema#date> |
inventor | http://rdf.ncbi.nlm.nih.gov/pubchem/patentinventor/MD5_088f5778ade47351302ef7ba68436574 http://rdf.ncbi.nlm.nih.gov/pubchem/patentinventor/MD5_36f3e0a81dc11d8e21d5b34484f74f41 http://rdf.ncbi.nlm.nih.gov/pubchem/patentinventor/MD5_6be1be3442fbe8704227990d887e5d23 |
publicationDate | 2022-07-08-04:00^^<http://www.w3.org/2001/XMLSchema#date> |
publicationNumber | CN-114717484-A |
titleOfInvention | A new type of high-silicon and high-chromium high-manganese steel and preparation method thereof |
abstract | The invention discloses a novel high-chromium, high-silicon and high-manganese steel and a preparation method thereof. The weight percentages of the chemical components of the high-manganese steel are: C: 0.4-1.1%, Mn: 13-20%, Cr: 3- 7%, Si: 2~4%, S≤0.04%, P≤0.03%, Mo: 0.5‑0.9%, V: 0.1‑0.2%, Ti: 0.08‑0.15%, Cu: 0.2‑ 0.6%, the rest is Fe. In the novel high manganese steel of the present invention, Si-Ca alloy is added in the pouring process after smelting: 0.25-0.4%. The heat treatment process of the casting is as follows: the solution treatment temperature is 1080-1180°C, the workpiece is released after the heat preservation is completed, and when the surface temperature of the workpiece is 1020-1050°C, it is immediately water-cooled until the temperature of the casting is room temperature-120°C, and the water is discharged, and then the workpiece is placed in Hold in a resistance furnace at 200-230°C for 3-5 hours. High-manganese steel has single-phase austenite, close-packed hexagonal martensite (ε-martensite) and austenite complex structure after heat treatment, and a small amount of body-centered cubic martensite (α'-martensite) may also exist. body). The mechanical properties are as follows: the yield strength is 460-600MPa, the tensile strength is 980-1100MPa, and the U-notch impact toughness is 162-320J/cm 2 . |
priorityDate | 2021-01-06-04:00^^<http://www.w3.org/2001/XMLSchema#date> |