http://rdf.ncbi.nlm.nih.gov/pubchem/patent/CN-113428942-B
Outgoing Links
Predicate | Object |
---|---|
classificationCPCAdditional | http://rdf.ncbi.nlm.nih.gov/pubchem/patentcpc/C02F2001-46142 |
classificationCPCInventive | http://rdf.ncbi.nlm.nih.gov/pubchem/patentcpc/C02F1-46109 http://rdf.ncbi.nlm.nih.gov/pubchem/patentcpc/C02F1-4672 |
classificationIPCInventive | http://rdf.ncbi.nlm.nih.gov/pubchem/patentipc/C02F1-461 http://rdf.ncbi.nlm.nih.gov/pubchem/patentipc/C02F1-467 |
filingDate | 2021-06-07-04:00^^<http://www.w3.org/2001/XMLSchema#date> |
grantDate | 2022-09-20-04:00^^<http://www.w3.org/2001/XMLSchema#date> |
publicationDate | 2022-09-20-04:00^^<http://www.w3.org/2001/XMLSchema#date> |
publicationNumber | CN-113428942-B |
titleOfInvention | A kind of noble metal low temperature coated titanium electrode and preparation method thereof |
abstract | The invention discloses a noble metal low-temperature coated titanium electrode and a preparation method thereof. The electrode is formed by fully mixing main materials and auxiliary materials with alkali metal or rare earth element ultrafine powder, the outer side of the electrode is coated with a coating, and the The coating is divided into the bottom layer, the middle layer and the surface layer; after fully mixing the main material and the auxiliary material, as the precious metal powder carrier material, the gold metal oxide powder is dispersed with a thermosetting resin, and is cured and sintered in different temperature zones, so that the The precious metal coatings are fused with each other. After the coating is formed, the film formation and thickness are higher than those of the anode bottom layer, middle layer and surface layer prepared by thermal decomposition. After the surface layer is sprayed, the coating is annealed and sintered at a temperature of 250‑400℃ and a time of 10‑ 30 minutes. Compared with the existing coated electrode, the coating significantly reduces the content of the noble metal iridium, avoids the influence caused by the fluctuation of the noble metal market, and at the same time ensures the use performance of the anode. |
priorityDate | 2021-06-07-04:00^^<http://www.w3.org/2001/XMLSchema#date> |