http://rdf.ncbi.nlm.nih.gov/pubchem/patent/CN-113003604-B
Outgoing Links
Predicate | Object |
---|---|
classificationCPCAdditional | http://rdf.ncbi.nlm.nih.gov/pubchem/patentcpc/C01P2004-61 http://rdf.ncbi.nlm.nih.gov/pubchem/patentcpc/C01P2004-30 |
classificationCPCInventive | http://rdf.ncbi.nlm.nih.gov/pubchem/patentcpc/C01G23-053 |
classificationIPCInventive | http://rdf.ncbi.nlm.nih.gov/pubchem/patentipc/C01G23-053 |
filingDate | 2021-03-19-04:00^^<http://www.w3.org/2001/XMLSchema#date> |
grantDate | 2022-06-17-04:00^^<http://www.w3.org/2001/XMLSchema#date> |
publicationDate | 2022-06-17-04:00^^<http://www.w3.org/2001/XMLSchema#date> |
publicationNumber | CN-113003604-B |
titleOfInvention | Preparation method of micron-sized titanium dioxide hollow blade |
abstract | The invention discloses a preparation method of titanium dioxide, which comprises the following steps: 1) mixing 0.1-10 parts of p-methyl phenethylamine, 0.5-5 parts of polyethylene-polypropylene glycol and 10-50ml of water and stirring to obtain a solution 1; 2) mixing a solution obtained by adding 10-50ml of water into 1-5 parts by weight of zinc nitrate hexahydrate, 0.5-7 parts by weight of hexamethylenetetramine, 0.3-3 parts by weight of cobalt nitrate hexahydrate and 1-10 parts by weight of 2-methylimidazole, and standing at normal temperature to obtain a solution 2; 3) while stirring the solution 2, adding 0.2-0.7 parts (by weight) of n-butyl titanate, and stirring to obtain a solution 3; 4) carrying out hydrothermal treatment on the solution 3; 5) and 4) carrying out centrifugal separation on the mixture in the step 4) to obtain titanium dioxide. The titanium dioxide structure of the invention not only achieves a safer micron-scale structure size, but also widens the active surface of catalytic reaction through a hollow structure. |