abstract |
The present invention provides a ferritic stainless steel hot-rolled and annealed steel sheet having excellent surface properties after bending. A ferritic stainless steel hot-rolled and annealed steel sheet containing, in mass %, C: 0.001-0.025%, Si: 0.05-0.70%, Mn: 0.05-0.50%, P: 0.050% or less, S: 0.01% or less, Cr: 10.0 to 18.0%, Ni: 0.01 to 1.00%, Al: 0.001 to 0.10%, N: 0.001 to 0.025%, Ti: 0.01 to 0.40%, the balance is composed of Fe and inevitable impurities, according to Measurement Method 1 The difference between the maximum value and the minimum value of the measured average grain size was 50 μm or less, the difference between the maximum value and the minimum value of the elongation of the crystal grains measured by the measurement method 2 was 5.0 or less, and the plate thickness was 5.0 mm or more. |