http://rdf.ncbi.nlm.nih.gov/pubchem/patent/CN-110627372-B
Outgoing Links
Predicate | Object |
---|---|
classificationCPCAdditional | http://rdf.ncbi.nlm.nih.gov/pubchem/patentcpc/C03C2217-241 http://rdf.ncbi.nlm.nih.gov/pubchem/patentcpc/C03C2218-32 http://rdf.ncbi.nlm.nih.gov/pubchem/patentcpc/C03C2218-114 http://rdf.ncbi.nlm.nih.gov/pubchem/patentcpc/C03C2217-24 |
classificationCPCInventive | http://rdf.ncbi.nlm.nih.gov/pubchem/patentcpc/C03C17-3417 http://rdf.ncbi.nlm.nih.gov/pubchem/patentcpc/G02F1-1523 http://rdf.ncbi.nlm.nih.gov/pubchem/patentcpc/G02F1-1524 |
classificationIPCInventive | http://rdf.ncbi.nlm.nih.gov/pubchem/patentipc/G02F1-15 http://rdf.ncbi.nlm.nih.gov/pubchem/patentipc/C03C17-34 |
filingDate | 2019-09-30-04:00^^<http://www.w3.org/2001/XMLSchema#date> |
grantDate | 2022-03-04-04:00^^<http://www.w3.org/2001/XMLSchema#date> |
publicationDate | 2022-03-04-04:00^^<http://www.w3.org/2001/XMLSchema#date> |
publicationNumber | CN-110627372-B |
titleOfInvention | Method for preparing lithium titanate electrochromic film |
abstract | The invention relates to a method for preparing a lithium titanate electrochromic film, which comprises the following steps: taking a lithium salt solution and an organic titanium salt solution, and mixing the solutes of the lithium salt solution and the organic titanium salt solution according to the mass ratio of the lithium salt solution to the organic titanium salt solution: uniformly mixing organic titanium salt (1-1.5) and 1 to obtain solution A; according to the quantity ratio of solute substances, oxalic acid: adding oxalic acid solution into the solution A, and uniformly mixing to form a lithium titanate sol precursor; taking a substrate containing a transparent conductive layer, coating a lithium titanate sol precursor on the surface of the transparent conductive layer of the substrate, and drying to prepare a lithium titanate sol precursor film; calcining the lithium titanate sol precursor film at the calcining temperature of 350-700 □ for 1-6 h, and cooling to obtain the lithium titanate electrochromic film. The method is simple to operate, and compared with the traditional color-changing layer material, the prepared electrochromic film has the advantages that the cycle performance, the service life and other performances of the color-changing layer material are greatly improved by applying the lithium titanate material. |
priorityDate | 2019-09-30-04:00^^<http://www.w3.org/2001/XMLSchema#date> |