http://rdf.ncbi.nlm.nih.gov/pubchem/patent/CN-109837536-A
Outgoing Links
Predicate | Object |
---|---|
assignee | http://rdf.ncbi.nlm.nih.gov/pubchem/patentassignee/MD5_04a4a10ec9ea68fdadca9350b9fa8d18 |
classificationIPCInventive | http://rdf.ncbi.nlm.nih.gov/pubchem/patentipc/C22C1-10 http://rdf.ncbi.nlm.nih.gov/pubchem/patentipc/C22C1-02 http://rdf.ncbi.nlm.nih.gov/pubchem/patentipc/C09D123-00 http://rdf.ncbi.nlm.nih.gov/pubchem/patentipc/C22C21-00 http://rdf.ncbi.nlm.nih.gov/pubchem/patentipc/C23C22-38 http://rdf.ncbi.nlm.nih.gov/pubchem/patentipc/B05D7-24 http://rdf.ncbi.nlm.nih.gov/pubchem/patentipc/B05D7-14 http://rdf.ncbi.nlm.nih.gov/pubchem/patentipc/C09D5-08 http://rdf.ncbi.nlm.nih.gov/pubchem/patentipc/C09D123-28 |
filingDate | 2017-11-27-04:00^^<http://www.w3.org/2001/XMLSchema#date> |
inventor | http://rdf.ncbi.nlm.nih.gov/pubchem/patentinventor/MD5_257023599eaca03eecab846f8fa7b46e |
publicationDate | 2019-06-04-04:00^^<http://www.w3.org/2001/XMLSchema#date> |
publicationNumber | CN-109837536-A |
titleOfInvention | A kind of aluminium section for buildings method of modifying |
abstract | The present invention relates to the modification of aluminum profile more particularly to a kind of aluminium section for buildings method of modifying.It includes that aluminium ingot is smelted into liquid aluminium, and the titanium dioxide of zirconium package and the silica hybrid powder of zirconium package is added, is kept for 3-5 hours under melting temperature;It is poured under 1.1-1.5MPa pressure in 600 DEG C or more of mold, carries out cooling, keeps the temperature, demould out aluminum profile;Modifying agent: sodium fluoride 20-40 parts is prepared by weight, 30-60 parts of ammonium acid fluoride, 10-20 parts of potassium permanganate, 40-50 parts of potassium chromate, 15-25 parts of trbasic zinc phosphate, 8-18 parts of sodium nitrate, 5-12 parts of praseodymium chloride, 10-16 parts of ethylenediamine tetra-acetic acid, 7-14 parts of malic acid, 8-12 parts of sodium dodecyl benzene sulfonate, 6-13 parts of nickel sulfate, 15-25 parts of triethanolamine, reducing agent 5-10 parts by weight containing alkali metal, the chlorinated polypropylene or polyolefin substrate adhesion promoter of 7-13 parts of weight, 500-900 parts of water;It controls pH value 3-4 and obtains modifying agent;Carry out the dry modified aluminum profile of acquisition of two leaching two.Aluminum profile light prepared by the present invention is soft, corrosion resistance is superior, safety and environmental protection. |
isCitedBy | http://rdf.ncbi.nlm.nih.gov/pubchem/patent/CN-112391620-A |
priorityDate | 2017-11-27-04:00^^<http://www.w3.org/2001/XMLSchema#date> |
type | http://data.epo.org/linked-data/def/patent/Publication |
Incoming Links
Total number of triples: 71.