http://rdf.ncbi.nlm.nih.gov/pubchem/patent/CN-109174195-B
Outgoing Links
Predicate | Object |
---|---|
classificationCPCAdditional | http://rdf.ncbi.nlm.nih.gov/pubchem/patentcpc/C02F2305-10 |
classificationCPCInventive | http://rdf.ncbi.nlm.nih.gov/pubchem/patentcpc/B01J35-004 http://rdf.ncbi.nlm.nih.gov/pubchem/patentcpc/C02F1-30 http://rdf.ncbi.nlm.nih.gov/pubchem/patentcpc/B01J31-26 http://rdf.ncbi.nlm.nih.gov/pubchem/patentcpc/B01J31-06 |
classificationIPCInventive | http://rdf.ncbi.nlm.nih.gov/pubchem/patentipc/B01J31-26 http://rdf.ncbi.nlm.nih.gov/pubchem/patentipc/C02F1-30 |
filingDate | 2018-09-10-04:00^^<http://www.w3.org/2001/XMLSchema#date> |
grantDate | 2021-07-09-04:00^^<http://www.w3.org/2001/XMLSchema#date> |
publicationDate | 2021-07-09-04:00^^<http://www.w3.org/2001/XMLSchema#date> |
publicationNumber | CN-109174195-B |
titleOfInvention | Preparation method of organic-inorganic blend membrane |
abstract | According to the preparation method of the organic-inorganic blend membrane, a polyethylene glycol solution with the solid content of 0.5-1% is added into a polyurethane polymer solution with the mass fraction of 10-18% to obtain a uniformly dispersed polyethylene glycol-polyurethane solution; adding negative oxygen ion powder with solid content of 12-18%; coating on release paper, immersing in water, taking out after the organic-inorganic mixed solution is solidified into a film, cleaning, drying, and soaking the polyurethane-based film in silver nitrate solution to be adsorbed in a dark place; and sequentially adding a disodium hydrogen phosphate solution and hexadecyl trimethyl ammonium bromide into a silver nitrate solution, carrying out a light-resistant reaction, taking out the polyurethane-based film, cleaning and drying to obtain the organic-inorganic blend film. The invention has the following characteristics: 1. the catalytic performance of the catalyst is improved, the specific surface area of the reaction is increased, the reaction active sites are increased, the photo-corrosion is reduced, and the service life of the catalyst is prolonged; 2. the substrate material is safe, nontoxic and environment-friendly. |