http://rdf.ncbi.nlm.nih.gov/pubchem/patent/CN-108690298-B
Outgoing Links
Predicate | Object |
---|---|
classificationCPCAdditional | http://rdf.ncbi.nlm.nih.gov/pubchem/patentcpc/C08J2327-06 http://rdf.ncbi.nlm.nih.gov/pubchem/patentcpc/C08J2427-24 http://rdf.ncbi.nlm.nih.gov/pubchem/patentcpc/C08K5-58 |
classificationCPCInventive | http://rdf.ncbi.nlm.nih.gov/pubchem/patentcpc/C08J5-18 |
classificationIPCInventive | http://rdf.ncbi.nlm.nih.gov/pubchem/patentipc/C08L51-04 http://rdf.ncbi.nlm.nih.gov/pubchem/patentipc/C08J5-18 http://rdf.ncbi.nlm.nih.gov/pubchem/patentipc/C08L27-06 http://rdf.ncbi.nlm.nih.gov/pubchem/patentipc/C08L27-24 http://rdf.ncbi.nlm.nih.gov/pubchem/patentipc/C08K5-58 http://rdf.ncbi.nlm.nih.gov/pubchem/patentipc/C08L77-00 |
filingDate | 2018-06-26-04:00^^<http://www.w3.org/2001/XMLSchema#date> |
grantDate | 2020-09-15-04:00^^<http://www.w3.org/2001/XMLSchema#date> |
publicationDate | 2020-09-15-04:00^^<http://www.w3.org/2001/XMLSchema#date> |
publicationNumber | CN-108690298-B |
titleOfInvention | Polyvinyl chloride rolled film and preparation method thereof |
abstract | The invention relates to a polyvinyl chloride calendered film and a preparation method thereof, wherein the preparation method comprises the following steps: 1) melting and mixing the raw materials: the raw materials comprise, by weight: 100 parts of universal polyvinyl chloride resin; 1-30 parts of chlorinated polyvinyl chloride resin; 2) preplasticizing the product obtained in the step 1) to obtain a preplasticized product; 3) conveying the preplasticized product to a calender for calendering; the calendering step comprises: i) conveying the preplasticized product to a calendering mechanism, and enabling the preplasticized product to pass through a calendering roller, wherein the temperature of the calendering roller is 180-210 ℃, so as to obtain a calendered product; and ii) stripping the rolled product from the rolling roller by using a leading-out mechanism, and enabling the rolled product to sequentially pass through a first leading-out roller set and a second leading-out roller set, wherein the temperature of the first leading-out roller set is 20-50 ℃, and the temperature of the second leading-out roller set is 80-120 ℃. The polyvinyl chloride calendered film obtained by the method has better transparency and lower glossiness. |