http://rdf.ncbi.nlm.nih.gov/pubchem/patent/CN-108492997-B
Outgoing Links
Predicate | Object |
---|---|
classificationCPCAdditional | http://rdf.ncbi.nlm.nih.gov/pubchem/patentcpc/Y02E60-13 |
classificationCPCInventive | http://rdf.ncbi.nlm.nih.gov/pubchem/patentcpc/H01G11-36 http://rdf.ncbi.nlm.nih.gov/pubchem/patentcpc/H01G11-46 http://rdf.ncbi.nlm.nih.gov/pubchem/patentcpc/H01G11-24 http://rdf.ncbi.nlm.nih.gov/pubchem/patentcpc/H01G11-30 http://rdf.ncbi.nlm.nih.gov/pubchem/patentcpc/H01G11-86 |
classificationIPCInventive | http://rdf.ncbi.nlm.nih.gov/pubchem/patentipc/H01G11-46 http://rdf.ncbi.nlm.nih.gov/pubchem/patentipc/H01G11-36 http://rdf.ncbi.nlm.nih.gov/pubchem/patentipc/H01G11-86 http://rdf.ncbi.nlm.nih.gov/pubchem/patentipc/H01G11-30 http://rdf.ncbi.nlm.nih.gov/pubchem/patentipc/H01G11-24 |
filingDate | 2018-03-15-04:00^^<http://www.w3.org/2001/XMLSchema#date> |
grantDate | 2019-06-25-04:00^^<http://www.w3.org/2001/XMLSchema#date> |
publicationDate | 2019-06-25-04:00^^<http://www.w3.org/2001/XMLSchema#date> |
publicationNumber | CN-108492997-B |
titleOfInvention | Silk base flexible electrode material and preparation method thereof |
abstract | The present invention relates to a kind of preparation methods of silk base flexible electrode material, and the real silk fabric after degumming is activated in aqueous acetic acid;The real silk fabric after activation is soaked in manganese acetate aqueous solution again;Then potassium permanganate solution is added thereto and obtains the real silk fabric for being deposited with manganese dioxide after washing to neutrality;The real silk fabric for being deposited with manganese dioxide is immersed in the graphene oxide hydrosol and is handled, the real silk fabric for being combined with graphene oxide and manganese dioxide is obtained, the graphene oxide on real silk fabric surface is then reduced to graphene, obtain silk base flexible electrode material.Method provided by the invention overcomes the deficiencies in the prior art, and prepared silk base flexible electrode material had both had ventilative, flexible, the stretchable feature of silk fabric, while still having kept good chemical property in a stretched state. |