http://rdf.ncbi.nlm.nih.gov/pubchem/patent/CN-107663076-B
Outgoing Links
| Predicate | Object |
|---|---|
| classificationCPCAdditional | http://rdf.ncbi.nlm.nih.gov/pubchem/patentcpc/C04B2235-96 http://rdf.ncbi.nlm.nih.gov/pubchem/patentcpc/C04B2235-661 http://rdf.ncbi.nlm.nih.gov/pubchem/patentcpc/C04B2235-6565 http://rdf.ncbi.nlm.nih.gov/pubchem/patentcpc/C04B2235-3472 http://rdf.ncbi.nlm.nih.gov/pubchem/patentcpc/C04B2235-5232 http://rdf.ncbi.nlm.nih.gov/pubchem/patentcpc/C04B2235-3217 http://rdf.ncbi.nlm.nih.gov/pubchem/patentcpc/Y02P40-60 |
| classificationCPCInventive | http://rdf.ncbi.nlm.nih.gov/pubchem/patentcpc/C04B33-1352 http://rdf.ncbi.nlm.nih.gov/pubchem/patentcpc/C04B33-32 http://rdf.ncbi.nlm.nih.gov/pubchem/patentcpc/C04B33-36 http://rdf.ncbi.nlm.nih.gov/pubchem/patentcpc/C04B33-13 http://rdf.ncbi.nlm.nih.gov/pubchem/patentcpc/C04B33-132 |
| classificationIPCInventive | http://rdf.ncbi.nlm.nih.gov/pubchem/patentipc/C04B33-135 http://rdf.ncbi.nlm.nih.gov/pubchem/patentipc/C04B33-132 http://rdf.ncbi.nlm.nih.gov/pubchem/patentipc/C04B33-13 http://rdf.ncbi.nlm.nih.gov/pubchem/patentipc/C04B33-36 http://rdf.ncbi.nlm.nih.gov/pubchem/patentipc/C04B33-32 |
| filingDate | 2017-09-21-04:00^^<http://www.w3.org/2001/XMLSchema#date> |
| grantDate | 2020-09-01-04:00^^<http://www.w3.org/2001/XMLSchema#date> |
| publicationDate | 2020-09-01-04:00^^<http://www.w3.org/2001/XMLSchema#date> |
| publicationNumber | CN-107663076-B |
| titleOfInvention | A kind of low-cost, high-strength building ceramic sheet and preparation method |
| abstract | The invention provides a low-cost, high-strength building ceramic sheet and a preparation method. Fly ash is used as a silicon source, and a silicon solution is dispersed in a ceramic raw material in advance, and then a calcium hydroxide solution is added, so that the silicon solution and the calcium hydroxide are The plastic ceramic material is drawn to form calcium silicate fibers with a uniformly dispersed network. After the green body is formed, the calcium silicate fibers are gradually formed and endow the green body with higher strength, thereby overcoming the cost of products in the preparation of large-area ceramic sheets in the prior art. It is difficult to form a reinforced network by directly adding fiber reinforcement, which leads to the technical defects of low strength and easy breakage of the ceramic sheet. |