http://rdf.ncbi.nlm.nih.gov/pubchem/patent/CN-106955701-B
Outgoing Links
Predicate | Object |
---|---|
classificationCPCAdditional | http://rdf.ncbi.nlm.nih.gov/pubchem/patentcpc/B01D2257-708 |
classificationCPCInventive | http://rdf.ncbi.nlm.nih.gov/pubchem/patentcpc/B01D53-8687 http://rdf.ncbi.nlm.nih.gov/pubchem/patentcpc/C01B33-12 http://rdf.ncbi.nlm.nih.gov/pubchem/patentcpc/B01J23-58 http://rdf.ncbi.nlm.nih.gov/pubchem/patentcpc/B01J35-1061 http://rdf.ncbi.nlm.nih.gov/pubchem/patentcpc/B01J35-1023 |
classificationIPCInventive | http://rdf.ncbi.nlm.nih.gov/pubchem/patentipc/C01B33-12 http://rdf.ncbi.nlm.nih.gov/pubchem/patentipc/B01J35-10 http://rdf.ncbi.nlm.nih.gov/pubchem/patentipc/B01D53-86 http://rdf.ncbi.nlm.nih.gov/pubchem/patentipc/B01J23-58 http://rdf.ncbi.nlm.nih.gov/pubchem/patentipc/B01D53-44 |
filingDate | 2017-03-01-04:00^^<http://www.w3.org/2001/XMLSchema#date> |
grantDate | 2019-05-03-04:00^^<http://www.w3.org/2001/XMLSchema#date> |
publicationDate | 2019-05-03-04:00^^<http://www.w3.org/2001/XMLSchema#date> |
publicationNumber | CN-106955701-B |
titleOfInvention | One kind SiO containing aluminium2Load high dispersive Pt catalyst and its preparation method and application |
abstract | One kind SiO containing aluminium 2 High dispersive Pt catalyst and its preparation method and application is loaded, the ethanol solution containing PVP-Pt is uniformly mixed with dehydrated alcohol, the rodlike SiO containing aluminium of K modification is then added 2 , it is uniformly mixed, obtains mixed solution;After gained mixed solution is filtered, washed, is dried, 400-600 DEG C of roasting 4-7h in air atmosphere, then 400-600 DEG C of roasting 4-7h in a hydrogen atmosphere, obtains SiO containing aluminium 2 Load high dispersive Pt catalyst.The present invention is prepared by Dual Surfactants method, hydrothermal synthesis method, rear modification calorize method, ion-exchange, reduction of ethylene glycol method, colloid infusion process etc., Pt nanoparticle with high specific surface area, big Micropore volume and high degree of dispersion, there is good low-temperature catalytic oxidation performance to OVOCs, and material has fabulous reaction stability. |
priorityDate | 2017-03-01-04:00^^<http://www.w3.org/2001/XMLSchema#date> |