http://rdf.ncbi.nlm.nih.gov/pubchem/patent/CN-106732512-A
Outgoing Links
| Predicate | Object |
|---|---|
| assignee | http://rdf.ncbi.nlm.nih.gov/pubchem/patentassignee/MD5_9aea490eb2a4a9a51e7b126e662c2135 |
| classificationCPCAdditional | http://rdf.ncbi.nlm.nih.gov/pubchem/patentcpc/C02F2305-10 |
| classificationCPCInventive | http://rdf.ncbi.nlm.nih.gov/pubchem/patentcpc/B01J35-004 http://rdf.ncbi.nlm.nih.gov/pubchem/patentcpc/C02F1-30 http://rdf.ncbi.nlm.nih.gov/pubchem/patentcpc/B01J23-06 |
| classificationIPCInventive | http://rdf.ncbi.nlm.nih.gov/pubchem/patentipc/C02F1-30 http://rdf.ncbi.nlm.nih.gov/pubchem/patentipc/B01J23-06 |
| filingDate | 2016-11-18-04:00^^<http://www.w3.org/2001/XMLSchema#date> |
| inventor | http://rdf.ncbi.nlm.nih.gov/pubchem/patentinventor/MD5_07aea3c31fd31480f25fa004746a5a90 |
| publicationDate | 2017-05-31-04:00^^<http://www.w3.org/2001/XMLSchema#date> |
| publicationNumber | CN-106732512-A |
| titleOfInvention | The preparation method of metal net surface ZnO nanorod |
| abstract | The present invention relates to a kind of preparation method of metal net surface ZnO nanorod.The preparation method of metal net surface ZnO nanorod, cleans each 20min, in an oven dry for standby with deionized water, acetone and EtOH Sonicate respectively by wire netting substrate；By 0.03 gZn (Ac) 2 It is dissolved in 11g absolute ethyl alcohols, the min obtained solutions of ultrasonic agitation 30；Wire netting is lifted rapidly after impregnating 30s in above-mentioned solution, is placed in baking oven and is dried, and above procedure is continuously repeated 5 times；Then preheated in Muffle furnace, be warming up to 600 DEG C of annealings, ZnO crystal seed layers are prepared in metal net surface；The wire netting growth for there are ZnO crystal seed layers will be prepared downwards, the Zn (NO of equimolar concentration are positioned over 3 ) 2 In HMTA growth solutions, 95 DEG C of water-bath 4h synthesize ZnO nanorod；（3）After the completion of reaction, print is cleaned with deionized water, dried in baking oven.ZnO nanorod photocatalytic activity prepared by the present invention is more excellent, and shows the good property of can be recycled. |
| isCitedBy | http://rdf.ncbi.nlm.nih.gov/pubchem/patent/CN-108553692-A |
| priorityDate | 2016-11-18-04:00^^<http://www.w3.org/2001/XMLSchema#date> |
| type | http://data.epo.org/linked-data/def/patent/Publication |
Incoming Links
Total number of triples: 24.