http://rdf.ncbi.nlm.nih.gov/pubchem/patent/CN-106637151-B
Outgoing Links
Predicate | Object |
---|---|
classificationCPCInventive | http://rdf.ncbi.nlm.nih.gov/pubchem/patentcpc/C23C18-1806 http://rdf.ncbi.nlm.nih.gov/pubchem/patentcpc/C23C18-36 http://rdf.ncbi.nlm.nih.gov/pubchem/patentcpc/C23C18-1837 |
classificationIPCInventive | http://rdf.ncbi.nlm.nih.gov/pubchem/patentipc/C23C18-18 http://rdf.ncbi.nlm.nih.gov/pubchem/patentipc/C23C18-36 |
filingDate | 2016-09-21-04:00^^<http://www.w3.org/2001/XMLSchema#date> |
grantDate | 2018-09-21-04:00^^<http://www.w3.org/2001/XMLSchema#date> |
publicationDate | 2018-09-21-04:00^^<http://www.w3.org/2001/XMLSchema#date> |
publicationNumber | CN-106637151-B |
titleOfInvention | A kind of preparation method for the aero titanium alloy that friction coefficient is high |
abstract | The invention discloses a kind of preparation methods for the aero titanium alloy that friction coefficient is high, include the following steps:A, the cleaning step of titanium alloy;B, the electroless plating step of titanium alloy, the chemical plating are Ni P Si C composite electroless-platings, i.e., cleaned titanium alloy are put into composite plating bath and carry out chemical plating, the condition of chemical plating is:Plating temperature is 80 90 DEG C, and PH is 6.5 7.5, and mixing speed is 10 20 revs/min, and plating solution useful load is 0.8 1.5dm 2 / L, plating time 0.5 1 hours.Compared with prior art, the present invention by selecting stabilizer, the phosphorus content for the titanium alloy that chemistry plates out is 3.23 3.28%, and hardness is 800 840HV, and friction coefficient is 0.7 0.75, and the stability of plating solution is good, and the service life of prepared plating solution is 2 2.5 hours. |